Ferromanganese

Ferromanganese, a ferroalloy with high content of manganese, is made by heating a mixture of the oxides MnO2 and Fe2O3, with carbon, usually as coal and coke, in either a blast furnace or an electric arc furnace-type system, called a submerged arc furnace. The oxides undergo carbothermal reduction in the furnaces, producing the ferromanganese. Ferromanganese is used as a deoxidizer for steel.

Henry Bessemer invented the use of ferromanganese as a method of introducing manganese in controlled proportions during the production of steel. The advantage of combining powdered iron oxide and manganese oxide together is the lower melting point of the combined alloy compared to pure manganese oxide.

A North American standard specification is ASTM A99. The ten grades covered under this specification includes;

A similar material is a pig iron with high content of manganese, is called spiegeleisen.

History

Evolution of global manganese production, by processes.

In 1872 Lambert von Pantz produced ferromanganese in a blast furnace, with significantly higher manganese content than was previously possible (37% instead of the previous 12%). This won his company international recognition, including a gold medal at the 1873 World Exposition in Vienna and a certificate of award at the Centennial Exposition in Pennsylvania in 1876.[1][2]

References

  1. ↑ Hočevar, Toussaint (1965). The structure of the Slovenian economy, 1848-1963. Studia Slovenica. p. 30. COBISS 26847745.
  2. ↑ Vilman, Vladimir (2004). "Von Pantzove gravitacijske žičnice na Slovenskem" [Von Pantnz's gravity ropeways in Slovenia]. Mednarodno posvetovanje Spravilo lesa z žičnicami za trajnostno gospodarjenje z gozdovi [International Symposium Cable Yarding Suitable for Sustainable Forest Management] (PDF) (in Slovenian and English). pp. 9–33.
This article is issued from Wikipedia - version of the 12/28/2015. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.