Shot (pellet)

Shot is a collective term for small balls or pellets, often made of lead. These were the original projectiles for shotguns and are still fired primarily from shotguns, although shot shells are available in many pistol calibers in a configuration called "bird shot", "rat-shot", or "snake shot". Lead shot is also used for a variety of other purposes such as filling cavities with dense material for weight/balance. Some versions may be plated with other metals. Lead shot was originally made by pouring molten lead through screens into water, forming what was known as "swan shot", and, later, more economically mass-produced at higher quality using a shot tower. The Bliemeister method has supplanted the shot tower method since the early 1960s.

Manufacture

Shot tower at Clifton Hill, Melbourne, Australia

Producing lead shot from a shot tower was pioneered by William Watts of Bristol who adapted his house on Redcliffe Way by adding a three-storey tower and digging a shaft under the house through the caves underneath to achieve the required drop. The process was patented in 1782.[1] The process was later brought above ground through the building of shot towers.

Molten lead would be dropped from the top of the tower. Like most liquids, surface tension makes drops of molten lead become near-spherical as they fall. When the tower is high enough, the lead droplets will solidify while still dropping and thus will retain their spherical form. Water is usually placed at the bottom of the tower, causing the lead to be cooled immediately after dropping.

Roundness of manufactured shot produced from the shot tower process is graded by forcing the newly produced shot to roll accurately down inclined planes. Unround shot will naturally roll to the side, for collection. The unround shot was either re-processed in another attempt to make round shot using the shot tower again, or used for applications which did not require round shot (e.g., split shot).[1]

The hardness of lead shot is controlled through adding variable amounts of tin, antimony and arsenic, forming alloys.[1] This also affects its melting point. Hardness is also controlled by the rate of cooling that is used in manufacturing lead shot.

The Bliemeister method, named for inventor Louis W. Bliemeister of Los Angeles, CA, (U.S. Patent 2,978,742, dated April 11, 1961) is a process for making lead shot in small sizes from about #7 through about #9. In this process, molten lead is dripped from small orifices and dropped approximately 1 inch (2.5 centimetres) into a hot liquid, where it is then rolled along an incline and then dropped another 3 ft (91 cm). The temperature of the liquid controls the cooling rate of the lead, while the surface tension of the liquid and the inclined surface(s) work together to bring the small droplets of lead into highly regular balls of lead in spherical form. The size of the lead shot that is produced is determined by the diameter of the orifice used to drip the lead, ranging from approximately 0.018-inches for #9 lead shot to about 0.025-inches for #6 or #7.0 shot, while also depending on the specific lead alloy that is used. The roundness of the lead shot depends on the angle of the inclined surfaces as well as the temperature of the liquid coolant. Various coolants have successfully been used, ranging from diesel fuel to antifreeze and water-soluble oil. After the lead shot cools, it is washed, then dried, and small amounts of graphite are finally added to prevent clumping of the lead shot. Lead shot larger than about #5 tends to clump badly when fed through tubes, even when graphite is used, whereas lead shot smaller than about #6 tends not to clump when fed through tubes when graphite is used.

Lead shot dropped quickly into liquid cooling baths when being produced from molten lead is known as "chilled lead shot", in contrast to "soft lead shot" which is produced by molten lead not being dropped as quickly into a liquid cooling bath. The process of rapidly chilling lead shot during its manufacturing process causes the shot to become harder than it would otherwise be if allowed to cool more slowly. Hence, chilled lead shot, being harder and less likely to deform during firing, is preferred by shotgunners for improving shot pattern densities at longer (> 30 yard) ranges, whereas soft lead shot, being softer and more likely to deform during firing, is preferred for improving shot pattern densities at very close (< 20 yard) ranges as the softer and now deformed shot scatters more quickly when fired. Soft lead shot is also more readily deformed during the firing process by the effects of chokes.

The manufacture of non-lead shot differs from that of lead, with compression molding used to create some alloys.[2]

Sizes

Shot is available in many sizes for different applications. The size of numbered shot decreases as the number increases. In hunting, some sizes are traditionally used for certain game, or certain shooting situations, although there is overlap and subjective preference. The range at which game is typically encountered and the penetration needed to assure a clean kill must both be considered. Local hunting regulations may also specify a size range for certain game. Shot loses its velocity very quickly due to its low sectional density and ballistic coefficient (see external ballistics). Generally, larger shot carries farther, and does not spread out as much as smaller shot.

Buckshot

Buckshot is simply shot formed to larger diameters so that it can be used against bigger game such as deer. Sizes range in ascending order from size #B to Tri-Ball. It is usually referred by the size, followed by "buck", e.g. "#000" is referred to as "triple-aught buck" in America or "triple o buck" in other English speaking countries. Buckshot is traditionally swaged (in high volume production) or cast (in small volume production). The Bliemeister method does not work for shot larger than #5, and works progressively poorly for shot sizes larger than about #6.

Lead shot comparison chart

Below is a chart with diameters per pellet and weight for idealized lead spheres.

Size Type Weight Diameter
0000 Buck 82 grains 9.70 mm (0.380")
000½ Buck 76 grains 9.40 mm (0.370")
000 Buck 70 grains 9.14 mm (0.360")
00½ Buck 59 grains 8.60 mm (0.340")
00 Buck 53.8 grains 8.38 mm (0.330")
0 Buck 49 grains 8.13 mm (0.320")
#1½ Buck 44.7 grains 7.90 mm (0.310")
#1 Buck 40.5 grains 7.62 mm (0.300")
#2½ Buck 36.6 grains 7.4 mm (0.290")
#2 Buck 29.4 grains 6.86 mm (0.270")
#3½ Buck 26.3 grains 6.60 mm (0.260")
#3 Buck 23.4 grains 6.35 mm (0.250")
#4 Buck 20.7 grains 6.09 mm (0.240")
FF Waterfowl 18.2 grains 5.84 mm (0.230")
F (or TTT)Waterfowl 16.0 grains 5.59 mm (0.220")
TT Waterfowl 13.9 grains 5.33 mm (0.210")
T Waterfowl 12.0 grains 5.08 mm (0.200")
BBB Bird 10.2 grains 4.82 mm (0.190")
BB Bird 8.50 grains 4.60 mm (0.180")
BB (air gun) Bird 8.10 grains 4.57 mm (0.177")
B Bird 7.40 grains 4.50 mm (0.170")
#1 Bird 6.15 grains 4.10 mm (0.160")
#2 Bird 4.40 grains 3.76 mm (0.150")
#3 Bird 5.07 grains 3.6 mm (0.140")
#4 Bird 3.30 grains 3.28 mm (0.130")
#4½ Bird 2.90 grains 3.18 mm (0.125")
#5 Bird 2.60 grains 3.05 mm (0.120")
#6 Bird 2.00 grains 2.77 mm (0.110")
#7 Bird 1.50 grains 2.50 mm (0.100")
#7½ Bird 1.29 grains 2.39 mm (0.095")
#8 Bird 1.09 grains 2.26 mm (0.090")
#8½ Bird 0.97 grains 2.16 mm (0.085")
#9 Bird 0.75 grains 2.01 mm (0.080")
#10 Pest 0.51 grains 1.80 mm (0.070")
#11 Pest 0.32 grains 1.50 mm (0.060")
#12 Pest 0.19 grains 1.30 mm (0.050")
Dust Pest 0.10 grains or less 1.00 mm (0.040") or less

Applications outside firearms

Lead shot is also often used as ballast in various situations, especially where a dense, pourable weight is required. Generally, small shot is best for these applications, as it can be poured more like a liquid. Completely round shot is not required. When used as a pourable/mouldable weight, the shot may be left loose, or mixed with a bonding agent such as epoxy to contain and stabilize the pellets after they are poured. Some applications are:

Bird lead poisoning

X-ray of lead shot accumulated in the gizzard of a dead swan

Lead shot-related waterfowl poisonings were first documented in the US in the 1880s;[3] by 1919, the spent lead pellets from waterfowl hunting was positively identified as a major source of deaths of bottom-feeding waterfowl.[4][5][6] Once ingested, stomach acids and mechanical action cause the lead to break down and be absorbed into the body and bloodstream, resulting in death. "If a bird swallows only one pellet, it usually survives, although its immune system and fertility are likely to be affected. Even low concentrations of lead have a negative impact on energy storage, which affects the ability to prepare for migration."[7] Upland game birds such as mourning doves, ring-necked pheasants, wild turkey, northern bobwhite quail and chukars can also ingest lead and thus be poisoned when they feed on seeds.[8]

As scavengers, Californian condors eat carcasses of game that have been shot, but not retrieved, and with them any fragments of lead; this in turn increases the lead levels in their bodies, leading to secondary lead poisoning.[9] Among condors around the Grand Canyon, lead poisoning because of eating lead shot is the most frequently diagnosed cause of death.[9]

Restrictions on the use of lead

Depending on hunting laws, alternatives to lead shot are mandated for use by hunters in certain locations or when hunting migratory waterfowl and migratory birds or when hunting within U.S. federal waterfowl production areas, U.S. national wildlife refuges, or some state wildlife management areas. Lead shot is also banned within an eight-county area in California designated as the condor's range. As of 2011, thirty-five states prohibited lead shot use in such specially-specified areas when hunting. While hunting non-migratory or upland birds, as well as animals, in the United States, lead shot is generally approved, except within the specially-designated non-toxic shot pellet zones.[10]

In an effort to protect the condor, the use of projectiles containing lead has been banned for hunting deer, wild pig, elk, pronghorn antelope, coyotes, ground squirrels, and other non-game wildlife in areas of California designated as its range.[11] The bald eagle has similarly been shown to be affected by lead originating from dead or wounded waterfowl—the requirement to protect this species was one of the biggest factors behind laws being introduced in 1991 by the United States Fish and Wildlife Service to ban lead shot in migratory waterfowl hunting.[12]

Hunting restrictions have also banned the use of lead shot while hunting migratory waterfowl in at least 29 countries across by international agreement,[8] for example the Agreement on the Conservation of African-Eurasian Migratory Waterbirds.[7][13] Depending on hunting laws, alternatives to lead shot are mandated for use by hunters in some locations when hunting migratory birds, notably waterfowl. In the US, the restrictions are limited to migratory waterfowl, while Canadian restrictions are wider and apply (with some exceptions) to all migratory birds.[12] The hunting of upland migratory birds such as mourning doves was specifically excluded from the 1991 US restrictions as scientific evidence did not support their contribution to the poisoning of bald eagles.[12] In 1985, Denmark banned the use of lead in wetlands covered by the Ramsar Convention, later expanding this restriction to the whole country.[14] The use of lead has been banned for all hunting activities in the Netherlands as of 1992.[15]

The Missouri Department of Conservation introduced regulations in 2007 in some hunting areas requiring the use of non-toxic shot to protect upland birds.[8] Some clay pigeon ranges in the US have banned the use of lead after elevated levels of lead were found in waterfowl, small birds, mammals and frogs in their vicinity.[8]

Non-toxic alternatives to lead shot

Approved alternatives while hunting migratory waterfowl include pellets manufactured from steel, tungsten-iron, tungsten-polymer, tungsten-nickel-iron, and bismuth-tin in place of lead shot. In the United States, UK, Canada, and many western European countries (France as of 2006), all shot used for hunting migratory waterfowl must now be non-toxic, and therefore may not contain any lead.

Steel was one of the first widely used lead alternatives that the ammunition industry turned to.[16] But steel is one hundred times harder than lead, with only two-thirds its density, resulting in undesirable ballistic properties compared to lead.[17] Steel shot can be as hard as some barrels, and may therefore damage chokes on older firearms that were designed only for use with softer lead shot.[16] The higher pressures required to compensate for the lower density of steel may exceed the design limits of a barrel.

Within recent years, several companies have created non-toxic shot out of bismuth, tungsten, or other elements or alloys with a density similar to or greater than lead, and with a shot softness that results in ballistic properties that are comparable to lead. These shells provide more consistent patterns than steel shot and provide greater range than steel shot. They are also generally safe to use in older shotguns with barrels and chokes not rated for use with steel shot, such as for bismuth and tungsten-polymer (although not tungsten-iron) shot. (Unfortunately, all non-lead shot other than steel is far more expensive than lead, which has reduced its acceptance by hunters.)

Non-Toxic Shot Types Approved by the US Fish and Wildlife Service[18]
Approved shot type Percent Composition by Weight
Bismuth-tin 97% bismuth, and 3% tin
Iron (steel) Iron and carbon
Iron-tungsten Any proportion of tungsten, and >1% iron
Iron-tungsten-nickel >1% iron, any proportion of tungsten, and up to 40% nickel
Tungsten-bronze 51.1% tungsten, 44.4% copper, 3.9% tin, and 0.6% iron, or 60% tungsten, 35.1% copper, 3.9% tin, and 1% iron
Tungsten-iron-copper-nickel 40-76% tungsten, 10-37% iron, 9-16% copper, and 5-7% nickel
Tungsten-matrix 95.9% tungsten, 4.1% polymer
Tungsten-polymer 95.5% tungsten, 4.5% Nylon 6 or Nylon 11
Tungsten-tin-iron Any proportions of tungsten and tin, and >1% iron
Tungsten-tin-bismuth Any proportions of tungsten, tin, and bismuth.
Tungsten-tin-iron-nickel 65% tungsten, 21.8% tin, 10.4% iron, and 2.8% nickel
Tungsten-iron-polymer 41.5-95.2% tungsten, 1.5-52.0% iron, and 3.5-8.0% fluoropolymer

See also

References

  1. 1 2 3 Guruswamy, Sivaraman (1999). "XIV. Ammunition". Engineering Properties and Applications of Lead Alloys. CRC Press. pp. 569–570. ISBN 978-0-8247-8247-4.
  2. ↑ Sapp, Rick (2011). Reloading for Shotgunners (5th Edition). Krause Publications. p. 49. ISBN 1440226911.
  3. ↑ Pokras, M.; Kneeland, M. (Sep 2008). "Lead poisoning: using transdisciplinary approaches to solve an ancient problem". EcoHealth. 5 (3): 379–385. doi:10.1007/s10393-008-0177-x. ISSN 1612-9202. PMID 19165554.
  4. ↑ Federal Cartridge Company Waterfowl and Steel Shot Guide. Volume I; 1988.
  5. ↑ Sanderson, Glen C. and Frank C. Bellrose. 1986. A Review of the Problem of Lead Poisoning in Waterfowl. Illinois Natural History Survey, Champaign, Illinois. Special Publication 4. 34pp. full report from scholar.google.com (cache)
  6. ↑ A.M. Scheuhammer and S. L. Norris. 1996. "The ecotoxicology of lead shot and lead fishing weights" Ecotoxicology Vol. 5 Number 5 pp. 279-295
  7. 1 2 "Phasing Out The Use Of Lead Shot For Hunting In Wetlands: Experiences Made and Lessons Learned By AEWA Range States" (pdf). AEWA. 5 Nov 2009: 3. Retrieved 25 Mar 2013.
  8. 1 2 3 4 Lahner, Lesanna L.; Franson, J. Christian. "Lead Poisoning in Wild Birds" (pdf). USGS National Wildlife Health Center. p. 2. Retrieved 4 Apr 2013.
  9. 1 2 Green, E.; Hunt, G.; Parish, N.; Newton, I. (2008). Pizzari, Tom, ed. "Effectiveness of Action to Reduce Exposure of Free-Ranging California Condors in Arizona and Utah to Lead from Spent Ammunition". PLoS ONE (Free full text). 3 (12): e4022. Bibcode:2008PLoSO...3.4022G. doi:10.1371/journal.pone.0004022. PMC 2603582Freely accessible. PMID 19107211.
  10. ↑ Elizabeth Weise & Adam Belz (2011-08-23). "Iowa in middle of lead-shot skirmish". USA Today. Retrieved 3 Apr 2011.
  11. ↑ "Get the Lead Out (Protecting the Condor)". California Department of Fish and Game. Archived from the original on 30 July 2009. Retrieved 2009-07-28.
  12. 1 2 3 John John Edward Elliott, Christine Annette Bishop, Christy Morrissey (2011). Wildlife Ecotoxicology. Springer. pp. 371–372. ISBN 0387894322.
  13. ↑ "Protecting Waterfowl From Lead In Wetlands: A Practical Guide to the Lead Shot Regulations in Northern Ireland" (pdf). Ireland: Countryside Alliance. 24 Apr 2009. Retrieved 24 Mar 2013.
  14. ↑ de Klemm, Cyrille; Shine, Claire (1996). Legal Measures for the Conservation of Natural Areas. Council of Europe. p. 54. ISBN 9287130701.
  15. ↑ Socolow, R (1996). Industrial Ecology and Global Change. Cambridge University Press. p. 307. ISBN 0521577837.
  16. 1 2 Barnes, Frank C. (2009). Cartridges of the World: A Complete and Illustrated Reference for Over 1500 Cartridges. Gun Digest Books. p. 483. ISBN 1440213305.
  17. ↑ "Lead Poisoning in Waterbirds: Alternatives to Lead Shot". AEWA. Retrieved 25 Mar 2013.
  18. ↑ "Non Toxic Shot Regulations For Hunting Waterfowl and Coots in The U.S". US Fish and Wildlife Service. 4 Apr 2013. Retrieved 4 Apr 2013.

External links

Look up shot in Wiktionary, the free dictionary.
This article is issued from Wikipedia - version of the 10/18/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.