Vulcanized fibre

Formed fishpaper (electrical grade vulcanized fibre) insulating shield.

Vulcanized fibre is a laminated plastic composed of only cellulose. The material is a tough, resilient, hornlike material that is lighter than aluminium, tougher than leather, and stiffer than most thermoplastics. The newer wood-laminating grade of vulcanized fibre is used to strengthen wood laminations used in skis, skateboards, support beams and as a sub-laminate under thin wood veneers.

A product very similar to vulcanized fibre is leatheroid. Leatheroid, however, is made using a different chemical process.

History

The British patent for vulcanized fibre was obtained in 1859 by the Englishman Thomas Taylor.[1] He gained the patent after the introduction of celluloid in 1856 and before the invention of viscose rayon (regenerated cellulose) in 1894. In 1871 Thomas Taylor obtained the United States Patent for vulcanized fibre.[2][3] The first organized industrial company to make vulcanized fibre, was the Vulcanized Fibre Company, incorporated first as a New York Corporation formed June 19, 1873 listed with William Courtenay President and Charles F. Cobby Secretary.[4] The first N.Y. corporation was also found in the 1873 N.Y. City Directory[5] which also listed William Courtenay President and Charles F. Cobby Secretary in 1873. From 1873 until 1878 the Vulcanized Fiber Co. had a New York office address of 17 Dey St., while the factory was located in Wilmington Delaware. This can be seen in the many advertisements that were placed in different publications at this time in history.[6] A special charter[7] was granted by the state of Delaware in 1873 until the Delaware corporation was finally incorporated on February 8, 1875 [8] which now listed William Courtenay President and Clement B. Smyth Secretary.

In 1884 Courtenay & Trull Co. N.Y. was merged into the Vulcanized Fibre Co.[9] which gave the company control over a new invention called by the trade name "Gelatinized Fibre".

On December 4, 1901, during a merger and consolidation the Vulcanized Fibre Co.[10] changed its name to the "American Vulcanized Fiber Co." which was formed for the purpose of consolidating: Kartavert Mfg. Company, Wilmington, Delaware; American Hard Fibre Company, Newark, Delaware; Vulcanized Fibre Company, Wilmington, Delaware. and the Laminar Fibre Company of North Cambridge, Mass.

In 1922 the name was changed again when it was directly purchased by the National Fibre & Insulation Company of Yorklyn Delaware (who was also the owner of the Keystone Fibre Co.). The president of the National Fibre Company at this time was J. Warren Marshall, who took the same office after consolidating into the new company "National Vulcanized Fibre Company.

In 1965 the name was changed again to the NVF Company in order to avoid confusion over the years with a new and changing product line.[11]

The water power of the Piedmont streams in Northern Delaware led to a proliferation of companies in the vulcanized fibre business. Over the years, these companies reorganized and merged. In 1922 National Vulcanized Fiber Company emerged as the main competitor to Spaulding Fibre, which had begun developing vulcanized products in Rochester, New Hampshire and Tonawanda, New York, nearly a quarter century after the industry began in Delaware.

Some of the companies involved in vulcanized fibre development in the Wilmington region were the Nunsuch Fiber Company, American Hard Fiber Company, American Vulcanized Fibre Company, Continental Fibre Co., Diamond State Fibre Co., and Franklin Fibre Company. In the 1965 Post’s Pulp and Paper Directory, National Vulcanized Fibre Co. was listed as having two mills' producing rag paper for vulcanized fibre. They were at Newark, producing 15 tons a day; and Yorklyn, producing 18 tons a day. This compares with Spaulding Fibre’s Tonawanda plant, then producing 40 tons a day (Post’s directory). The competitors also produced bakelite, but marketed them under different names: Spaulding’s was Spauldite and National’s brand was Phenolite and Iten Industries' Resiten or Itenite.

Process

The process started with paper made from cotton rags. Before the processing of wood pulp and chemical wood pulps in the mid-19th century, the dominant fibre source for paper making was cotton and linen rags. The cotton rag sheet produced for conversion to vulcanized fibre is made like a sheet suitable for saturating. A paper is made for saturating by omitting any sizing additive, either beater added or surface applied. Today most paper sheets made for writing, printing, and coating have internal (beater added) sizing provided by rosin, alkyl succinic anhydride (ASA), or alkyl ketene dimer (AKD) and surface sizing provided by starch. A sheet made for saturating would have none of those chemical ingredients. The unsized saturating cotton fibre paper prepared for vulcanized fibre would be passed through a vat containing a zinc chloride solution.

Zinc chloride

Zinc chloride is highly soluble in water. The solution used in saturating the paper was 70 Baume in density (1.93 specific gravity) and about 110°F.[12] This is roughly a 70% percent zinc chloride solution. Zinc chloride is a mild lewis acid with a solution pH of about 4. Zinc chloride can dissolve cellulose, starch, and silk. The zinc chloride used in making vulcanized fibre swelled and gelatinized the cellulose. The fibre swelling explains why paper filters cannot be used to filter zinc chloride solutions. It is also the reason why a number of paper plies were used to build up to the desired vulcanized fibre thickness, rather treating a single paperboard thickness. For instance, the practice was to use 8 paper plies of 4 mm thickness each, as opposed to a single paperboard ply of 32 mm.

Pressing

Once the paper plies were saturated with the gelatinizing zinc chloride, they were pressed together. The pressing allowed intimate contact of the cellulose fibres, thus promoting bonding between the cellulose chains. Once the bonding was established, the process of leaching out the zinc chloride from the vulcanized fibre could begin. The leaching (removal by diffusion out) of the zinc chloride was accomplished by subjecting the vulcanized fibre to successively less concentrated baths of zinc chloride. The rate at which this could occur was constrained by osmotic forces. If the rate at which the vulcanized fibre was subjected to lower and lower concentrations of zinc chloride solution were too rapid, the osmotic forces could result in ply separations. The final leaching bath concentration was 0.05% zinc chloride.Thicknesses up to 0.093”, can be made on continuous lines that stretch up to 1,000 feet (305m) in length.

Vats

For thickness above 0.093” and up to 0.375”, a discrete laminated sheet (similar in size (l x w) to plywood) was produced by the cutdown process. The cutdown sheets were racked and moved from vat to vat by overhead tracked cranes. Each vat was successively less concentrated until the desired 0.05% was reached. The thicker the material, the longer it took to leach the zinc chloride to 0.05%. For the thickest products, times of 18 months to 2 years were needed. The zinc chloride used in these processes was for the most part not consumed in achieving the desired bonding. Indeed any dilution of the zinc chloride resulting from the leaching was dealt with by using evaporators to bring the zinc chloride solution back to the 70 Baume needed for using it again for saturating. In a sense, zinc chloride can be thought of as a catalyst in the making of the vulcanized fibre.

Dried and pressed

Once the vulcanized fibre is leached free of the zinc chloride, it is dried to 5 to 6 percent moisture, and pressed or calendared to flatness. The continuous process-made vulcanized fibre could then be sheeted or wound up into rolls. The density of the finished vulcanized fibre is 2 to 3 times greater than the paper from which it starts. The density increase is the result of 10% machine direction shrinkage, 20% cross machine direction shrinkage, and 30% shrinkage in thickness.

Properties

The final product is a homogeneous nearly 100%-cellulose mass free from any artificial glues, resins, or binders. The finished vulcanized fibre has useful mechanical and electrical properties. It offers high tear and tensile strength, while in the thinner thicknesses allowing flexibility to conform to curves and bends. In thicker thicknesses, it can be moulded to shape with steam and pressure. One application for vulcanized fibre that attests to its physical strength is that it is the preferred material for heavy sanding discs. The electrical properties exhibited by vulcanized fibre are high insulating value, and arc and track resistance with service temperature of up to 110 to 120°C. Vulcanized fibre shows high resistance to penetration by most organic solvents, oils, and petroleum derivatives

Applications

References

  1. ↑ PIKE CREEK: INDUSTRY AND FARMING ALONG A NORTHERN DELAWARE RIVER; p 4-8.
  2. ↑ "PLASTICS HISTORY: Plastic Distributor & Fabricator", Plastics Magazine
  3. ↑ Taylor, Thomas, Improvement in the treatment of paper and paper-pulp, U.S. Patent 114,880, granted May 16, 1871.
  4. ↑ "History of the state of Delaware" Volume 2 Page 415
  5. ↑ The New York City register page 34
  6. ↑ Vulcanized Fibre Co. advertizements
  7. ↑ Industries of Delaware: historical and descriptive review : cities, towns and business interests, institutions, manufacturing and commercial advantages
  8. ↑ Laws of the state of Delaware, Volum 15
  9. ↑ Courtenay & Trull Co. N.Y. was merged into the Vulcanized Fibre Co.
  10. ↑ VULCANIZED FIBER COMPANY - MERGES INTO A NEW NAMEAMERICAN VULCANIZED FIBRE CO.
  11. ↑ Fiber Company History & Merger Tree
  12. ↑ James P. Casey, Pulp and Paper Chemistry and Chemical Technology; Vol. II; Second Edition Revised and Enlarged: Interscience Publishers Inc., New York, John Wiley & Sons Inc., New York; 1952, 1960; Library of Congress 60-13120; Third Printing 1967, pp654-655
This article is issued from Wikipedia - version of the 10/20/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.